What is the Difference Between Cold Chamber Casting and Hot Chamber Casting?

By Henry / July 5th, 2024 

Die casting is divided into cold chamber die casting and hot chamber die casting.

The difference between them is that hot chamber die casting is suitable for metals with low melting point and good fluidity, it has the characteristics of high 

efficiency production and good surface treatment, suitable for producing small parts, such as buttons on bags, decorations on toys, zippers on clothes, etc.

Zinc alloy die casting is suitable for hot chamber die casting, while cold chamber die casting is more suitable for metals with higher melting points and 

higher requirements for mechanical properties.

Cold chamber die casting is usually suitable for large parts for die casting production, such as automotive parts, aluminum pot production, lighting, and 

lock production, aluminum alloy die casting is a cold chamber die casting, do you understand?

For more info , pls refer to:https://youtu.be/m8HvtXqkyqQ?si=fkrRAwdevdOSZNij

Contact LK Egypt to learn more info about the die-casting machine

LKAGENT OFFICE DCM

Address: Industry Zone, South of Port Said Kebly, Egypt

https://www.zazdiecasting.com/

Phone: +86 13598704163

Mobile: +20 101 304 3317      +20 150 181 8310

Email: jack@zazmae.com      ahmedmahmoud@zazmae.com

#die cast tooling

#trivalent chromate

#rapid prototype casting

#a360 aluminum

#aluminum caster

#aluminum prototype

#ideal 55 slider parts

#density of aluminum kg/mm3

#magnesium sheet metal

#parts of a metal gate

#subcontracting of screw machining for the luxury sector

#wall aluminum

#die casting tooling

#tooling for die casting

#density of aluminium in kg mm3

#clear chromate

#es casting metals

#gating material

#prototype aluminum

#sigma castings

#subcontracting of screw-machining for household appliances

#we squeeze to please machine

#aluminium gravity die casting

#aluminum part

#aluminum rapid prototyping

#nickel casting

#plunger tip for die casting machine

#rapid prototyping aluminium